Borealis PP HJ325MO
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wy6apY_Borealis-PP-HJ325MO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HJ325MO is a polypropylene homopolymer intended for injection moulding. Its very high melt flow makes it especially suitable for thin-wall packaging and products with long flow length. is designed for high-speed injection moulding and contains nucleating and antistatic additives. The additives are optimized to provide reduced tendency for mould plate-out. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Components moulded from this grade show good ejectability and combine good stiffness with good transparency and gloss, good antistatic properties and good impact strength at ambient temperatures. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 50 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 to 2.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 103 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 250 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 20.0 to 50.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Injection molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AS30BK6328 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| LARIPUR® LPR 5520 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Karina MBU LILAC E 34/160-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS DFR218 | AD majoris | PP, Unspecified | MAJORIS |
| Lucofin® 1492M | Lucobit AG | EBA | Lucofin® |