Stanyl® TW241B3
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wxk2we_Stanyl-TW241B3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TW241B3 is a Polyamide 46 (Nylon 46) material filled with 15% carbon fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TW241B3 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.22 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 13000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 185 | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 10500 | 5800 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.5 | 4.5 | kJ/m² | |
| 23°C | 5.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 45 | 70 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 4.5 | 4.5 | kJ/m² | |
| 23°C | 5.0 | 12 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6003-45A MD NATURAL | RTP Company | TPE | RTP |
| REVOLVE® N-250 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| TITANLENE® LDF 260JG | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Multi-Flex® TPE A5904 LC | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| ISOPAK® 525GF17 | Great Eastern Resins Industrial Co., Ltd. (GRECO) | ABS | ISOPAK® |