Maxxam™ PPR-20G Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wv7bbu_Maxxam-PPR-20G-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene and Polyethylene Based Maxxam™The product line is suitable for a variety of applications and performance requirements. After the standard product is mixed with calcium carbonate, glass and talcum powder, all the properties are ideal, including rigidity, durability, impact resistance and heat resistance. Customized products have many uses, such as: ultraviolet stabilizer, heat stabilizer, color customization, impact resistance products, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Specific Volume | 0.961 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 64.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 3520 | MPa | ASTM D790 |
| Flexural Strength | 90.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 69 | J/m | ASTM D256A |
| Unnotched Izod Impact 4(23°C, 3.18 mm) | 310 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 157 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | HB | UL 94 |
| Additional Information |
|---|
| Product Code: EM00901245** |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 16.0 - 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type 1, 51mm/min |
| 3 . | Type 1, 51mm/min |
| 4 . | Injection Molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MBF 6010 H | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| TAROPRENE® 1 A70 M1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| CYCOLAC™ INP563 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |
| Hydroxy-Purge 15C | InChem Corp. | TP, Unspecified | Hydroxy-Purge |
| SD POLYCA™ 877-20 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |