LNP™ LUBRICOMP™ SFP36 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wusFKG_LNP-LUBRICOMP-SFP36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound SFL-4536 Product reorder name: SFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.39 | g/cm³ | ASTM D792 |
| -- | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9060 | MPa | ASTM D638 |
| -- | 9070 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 125 | MPa | ASTM D638 |
| Yield | 129 | MPa | ISO 527-2/5 |
| Break 3 | 117 | MPa | ASTM D638 |
| Break | 129 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.3 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 5 | 3.3 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 7510 | MPa | ASTM D790 |
| -- 7 | 7930 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 191 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 178 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 176 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.67 | ||
| vs. Itself - Static | 0.53 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.200 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 10 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 11 | 59 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.90 | J | ASTM D3763 |
| -- | 3.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 177 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 177 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 172 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 169 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V976 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Nylfor® 74S5501PO 0001 | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| HIDEN® VH150U | YUHWA Korea Petrochemical Ind. Co., Ltd. | UHMWPE | HIDEN® |
| HiFill® PA6 GF20 L BK002 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Jackdaw PP ER14BK8003 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |