DOWLEX™ 2045.01 G
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wuRLyT_DOWLEX-2045-01-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX 2045.01G Polyethylene Resin is designed for the production of a wide variety of industrial and consumer films. Films made from this resin exhibit a combination of excellent toughness and tear resistance. The product also delivers very good processability on conventional LLDPE machinery. DOWLEX 2045.01G Polyethylene Resin contains slip and antiblock additives. Applications:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 19.0 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 346 | J/cm³ | ASTM D882 |
| TD : 51 µm | 351 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 194 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 233 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 55.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 50.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 830 | % | ASTM D882 |
| TD : Fracture, 51 µm | 890 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 290 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 900 | g | ASTM D1922 |
| TD : 51 µm | 1200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 51.0 µm) | 54 | ASTM D2457 | |
| Haze (51.0 µm) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| 薄膜和光学属性：吹塑薄膜，BUR 2.5。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 240 | °C |
| Extrusion instructions |
|---|
| 管形薄膜挤出的制造条件： 模具间隙：1.6 至 2.5 mm 熔体温度：190 至 240°C 放大比范围：1.50 至 3:1。 建议的厚度范围：10 至 150 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HT940UE | LyondellBasell Industries | PP Copolymer | Supol |
| HAIPLEN H30 G4 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| INELEC PA66CF20 | Infinity LTL Engineered Compounds | Nylon 66 | INELEC |
| LNP™ LUBRICOMP™ KAL22M compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| Sylvin 8381-75 Brown 7437 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |