INNOPOL® PP CS 1-5140 LH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wt01Bp_INNOPOL-PP-CS-1-5140-LH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-5140 LH is a 40 % talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/. This grade is available in nature and custom coloured form as well. INNOPOL® CS 1-5140 BLH is recommended especially for producing products, where high stiffness, low shrinkage and long term heat stability are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Ash Content (600°C) | 37 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.6 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 7.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 4100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.6 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 13 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 133 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 79.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A120 |
| -- | 93.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 190 - 240 | °C | |
| Front Temperature | 190 - 240 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G25 FR PRTA011 NR410 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| BESTPOLUX PCX-02 | Triesa Plastics | PC | BESTPOLUX |
| ELASTOSIL® AUX BATCH SB 2 | Wacker Chemie AG | Silicone | ELASTOSIL® AUX |
| INTEGRAL™ D200 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |
| LUBEMID B27 EL80 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |