Nypol® PA B3 G30 UV HS NTLA010 NT311
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wsIGCA_Nypol-PA-B3-G30-UV-HS-NTLA010-NT311.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 natural reinforced with 30% of fiberglass,UV protection, good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 to 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 | -- | % | ASTM D570 |
| Ash Content | 28 to 32 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 140 | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 7900 | 4700 | MPa | ASTM D790 |
| Flexural Strength | 220 | 190 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 120 | 180 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 180 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | 210 | -- | °C | ASTM D1525 1 |
| Melting Temperature | 210 to 225 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PS High Impact IS200 | M. Holland Company | PS (HIPS) | MTEGRITY™ PS High Impact |
| GAPEX® RPP30EU55HB BLACK | Ferro Corporation | PP Copolymer | GAPEX® |
| Karina FUM\u00C9 MBATCH (SP31452) -E 27/ 8-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ UX04509 compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| LEXAN™ 241R resin | SABIC Innovative Plastics | PC | LEXAN™ |