EMERGE™ PC 4310-22
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wrtwvK_EMERGE-PC-4310-22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 4310-22 Advanced Resin is a high-performance polycarbonate resin offering high heat resistance, toughness, and superior flow. This resin is available in a full range of colors that can be custom tailored to meet your product requirements. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2340 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 60.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 65.5 | MPa | |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 120 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 750 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm, Injection Molded) | No Break | ASTM D256 | |
| Instrumented Dart Impact 1(23°C, 3.20 mm, Injection Molded, Peak Energy) | 72.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.99 mm | 142 | °C | |
| 1.8 MPa, Unannealed, 3.99 mm | 126 | °C | |
| 1.8 MPa, Annealed, 3.99 mm | 139 | °C | |
| CLTE - Flow (-40 to 80°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index 3 | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | 3.39 m/sec |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200-80A TFE 15 | RTP Company | TPU-Polyester | RTP |
| Sindustris ABS LAF423C | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| LNP™ STAT-KON™ DEL32P compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| Sylvin 8377-75UV Black 2101 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9710-80FUV Orange 574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |