EVICOM™ RC7/748
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | INEOS Compounds |
| Trademark: | EVICOM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wrpckK_EVICOM-RC7-748.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description : Impact modified, tin stabilised, extrusion blow moulding bottle grade Application : Extrusions blow moulded bottles Specification : Complies with EEC directive 90/128/EEC for plastics in contact with foodstuffs VCM Content, EEC- 81/432CEE: <1 ppm |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | BS 2782 620A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (23°C) | 2800 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 45.0 | MPa | BS 2782 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 75.0 | °C | BS 2782 120B |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 0.16 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | BS 2782 |
| Volume Resistivity | 5.0E+14 | ohms·cm | BS 2782 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 6620 | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| Royalite R722 | Spartech Plastics | PMMA+PVC | Royalite |
| UBE Polyamide Elastomer XPA 9040F1 | UBE Industries, Ltd. | TPA-ET | UBE Polyamide Elastomer |
| Zytel® 80G14AHS BK099 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Durolon® VRY2000 | Unigel Plásticos | PC | Durolon® |