LEXAN™ LUX1814N resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wrUIV4_LEXAN-LUX1814N-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Grade for extrusion lighting applications meeting NSF requirements |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2300 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 91 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2370 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 830 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 72.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 127 | °C | ASTM D648 |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 - 87.8 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 166 | °C | |
| Cylinder Zone 2 Temp. | 171 | °C | |
| Cylinder Zone 3 Temp. | 177 | °C | |
| Cylinder Zone 4 Temp. | 182 | °C | |
| Melt Temperature | 182 - 199 | °C |
| Extrusion instructions |
|---|
| Minimum Moisture Content: .04%Roll Stack Temperature - Bottom: 177 - 182°CRoll Stack Temperature - Middle: 177 - 182°CRoll Stack Temperature - Top: 177 - 182°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN70100 | LyondellBasell Industries | LDPE | Microthene® G |
| Elastron® G P.G100.A70.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Polifil® Nylon 628BR-WO | The Plastics Group | Nylon 66 | Polifil® Nylon |
| Complet® LCF25-LGF25-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| Sylvin 6185-80 White 190 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |