Lustran® SAN DN59
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | INEOS ABS (USA) |
| Trademark: | Lustran® SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wqnV64_Lustran-SAN-DN59.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran SAN DN59 resin is a soft-flow grade of transparent SAN (styrene acrylonitrile) thermoplastic. It has been designed for use in compounding and thin-wall injection molded applications. Lustran SAN DN59 has a large molding window and is easy to process. It is available only in natural (000000) color. As with any product, use of Lustran SAN DN59 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Specific Volume | 0.930 | cm³/g | ASTM D792 |
| Acrylonitrile Content | 29.5 | % | |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4710 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 58.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3760 | MPa | ISO 178 |
| Flexural Stress 1 | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 1.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 106 | °C | ISO 306/A120 |
| -- | 99.5 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.0 - 88.0 | °C | |
| B | 71.0 - 77.0 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 170 - 185 | °C | |
| Middle Temperature | 185 - 200 | °C | |
| Front Temperature | 200 - 215 | °C | |
| Nozzle Temperature | 200 - 215 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 40 to 80% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP HDPE 003955PZ | Amco Polymers | HDPE | PRIMATOP |
| TRISTAR® PC-20GF | Polymer Technology and Services, LLC | PC | TRISTAR® |
| CP PRYME® Nylon 6 N233HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| ESTOPLAST XU 6215BB51 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| ALCOM® PC 740/4 UV WT1081-08LD2 | ALBIS PLASTIC GmbH | PC | ALCOM® PC |