Plenco 04485 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wqc3Tr_Plenco-04485-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 04485 is a mineral filled phenolic molding compound offering excellent heat resistance, electrical resistance, and dimensional stability. UL recognized under component file E40654. 04485 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.48 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9170 | MPa | ASTM D638 |
| Tensile Strength | 59.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 8510 | MPa | ASTM D790 |
| Flexural Strength | 93.8 | MPa | ASTM D790 |
| Compressive Strength | 207 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20.5 | J/m | ASTM D256 |
| Notched Izod Impact | 18 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 192 | °C | ASTM D648 |
| Continuous Use Temperature | 207 | °C | ASTM D794 |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.4E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 11 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.057 | ASTM D150 | |
| Arc Resistance | 137 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 150 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 | |
| Oxygen Index | 28 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.20%Drop Ball Impact, PLENCO Method: 107 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PE 1250 | Premix Oy | HDPE | PRE-ELEC® |
| SABIC® PPcompound 3020B | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| S&E PVC GA-1060 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Vipel® F701-FBN-28 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Borlink™ LE0310-99 | Borealis AG | TP, Unspecified | Borlink™ |