XAREC™ N WA 7020
| Category: | SPS+Nylon , Syndiotactic Polystyrene + Nylon |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | XAREC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wq9xp3_XAREC-N-WA-7020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XAREC™ N WA 7020 is a Syndiotactic Polystyrene + Nylon (SPS+Nylon) product filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.50 to 0.80 | % | |
| Flow | 0.30 to 0.60 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2 |
| Flexural Modulus | 6700 | MPa | ISO 178 |
| Flexural Stress | 215 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | °C | ISO 75-2/A |
| CLTE | TMA | ||
| Flow : -30 to 30°C | 3.0E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.4E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.1E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.034 | IEC 60250 | |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) 3 | PLC 1 | IEC 60112 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 5 | ||
| 3.00 mm | PLC 4 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (> 1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 1.0 to 3.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| 2 . | Mold temperature: 80°C |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP647N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| VITAMIDE® BF23GY6610 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| APEX® 3200-90NT | Teknor Apex Company | PVC, Flexible | APEX® |
| IPC PP 4830H-MLGF8-R2-UV | International Polymers Corporation | PP, Unspecified | IPC PP |
| Petrotene® PP A3 C45 MF NTLA010 PH381 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |