Hostacom X M2 T20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wpgvfg_Hostacom-X-M2-T20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" X M2 T20 is a 20% mineral filled, polypropylene copolymer for injection molding. It combines good stiffness/impact balance, good scratch resistance and low odor. The grade has been specifically designed for molding of automotive interior trim parts. The grade is available in color-matched, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 HF UV | RTP Company | PC | RTP |
| Axiall PVC HHP-190 FR Natural | Axiall Corporation | PVC Alloy | Axiall PVC |
| Grilon® TSZ 3 | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| Karina CLEAR PVC COMPOUND 800/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Zetpol® 2000 | Zeon Corporation | NBR | Zetpol® |