PROTEQ™ C23UST4Z
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wpfFNb_PROTEQ-C23UST4Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C23UST4Z is a high crystallinity, high melt flow polypropylene copolymer containing mineral filler which has been highly impact modified, heat stabilised and UV stabilised. PROTEQ™ C23UST4Z has been designed to meet the stringent requirements of automotive exterior trim durability specifications, combining easy processing with low temperature toughness, rigidity, heat resistance, hardness and improved marr resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 66 | ||
| Shore D, 15 sec | 59 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 17.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 150 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 280 | J/m | |
| 23°C, 3.20 mm | 580 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 126 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 57.0 | °C | |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 4 |
| CLTE - Flow | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA HDPE 1107 E | MBA Polymers | HDPE | MBA HDPE |
| Sindustris ABS LXR515T | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Ultracast II TC-1630 A/B | BJB Enterprises, Inc. | TSU | Ultracast II |
| LEXAN™ CFR5630D resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| SD POLYCA™ IM6011 | Sumika Styron Polycarbonate Limited | PC+ABS | SD POLYCA™ |