HOPELEX PCG-2305
| Category: | PC , Polycarbonate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | woZvC1_HOPELEX-PCG-2305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
30% glass-fiber reinforced, easy mold release Non-brominated, non-chlorinated flame retardant Optimum combination of high modulus and impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.25 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 137 | MPa | ASTM D638 |
| Flexural Modulus 2 | 7260 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 196 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 141 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 300 to 320 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | 300 to 320 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® PPs grey | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| Axiall PVC 22840 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| DAI-EL™ G-7261 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Kaneka MUH LG5012 | Kaneka Corporation | ABS | Kaneka MUH |
| LUVOCOM® 1-8218 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |