| Badamid® PA610 GF30 TF15 is a Polyamide 610 (Nylon 610) material filled with 30% glass fiber and 15% ptfe fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA610 GF30 TF15: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.4 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9100 | 8300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 140 | 125 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 23°C) | 2.5 | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Stress (23°C, 4.00 mm) | 200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 197 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1615 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Flexathene® TP38NC01X01 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Polifor® 25 GFCF/20 NERO | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Polifor® 5003/V2 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Sylvin 8980-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |