Crastin® HR5330HFS NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wo3iAB_Crastin-HR5330HFS-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced Polybutylene Terephthalate with Improved Processing |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.35 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 10 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 222 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 65.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 30 | mm/min | ISO 3795 |
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (250°C, 1000 sec^-1) | 230 | Pa·s | ISO 11443 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P50B03 | Polyram Ram-On Industries | PP Copolymer | Polytron® |
| Yuyao PP TL603 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| AKROMID® A3 1 FR black (3051) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| IROSTIC® S 6515 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| LUVOCOM® 1-8840 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |