WPP PP PPH1CF4-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wnZqQy_WPP-PP-PPH1CF4-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPH1CF4-Black is a polypropylene homopolymer (PP Homopoly) product, which contains 41% calcium carbonate filler. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 25.0 | MPa | ASTM D638 |
| Yield | 24.0 | MPa | ISO 527-2/5 |
| Yield | 25.0 | MPa | ISO 527-2/50 |
| Fracture 2 | 25.0 | MPa | ASTM D638 |
| Fracture | 21.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 240 | % | ASTM D638 |
| Fracture | 570 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 4 | 2500 | MPa | ASTM D790 |
| Tangent | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| -40°C | 3.0 | kJ/m² | ISO 180 |
| 23°C | 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 114 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, not annealed | 64.0 | °C | ISO 75-2/Af |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 A4G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| NEXT REGRIND PC 500-300RG | NEXT Specialty Resins, Inc. | PC | NEXT REGRIND |
| LG PMMA HP210 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| LNP™ KONDUIT™ PX11311U compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ KONDUIT™ |
| Hifax BC 72 A/1 3001 | LyondellBasell Industries | PP Copolymer | Hifax |