China PPS PTFE-hGR203
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wmitrt_China-PPS-PTFE-hGR203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS/PTFE-hGR203 is lubricant PPS compound, which is filled with glass fiber, PTFE and ingredients based on the PPS resin. It shows solvent resistance, abrasive resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage, good dimensional stability. Owing to its high performance, it's widely used in mechanical and chemical industry for making wearable parts/components which work in the high-temperature, high pressure and solvent circumstance. Such as: plastic axle bearing, axle sleeve, textile machine components, components which are used in aero industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | Internal method |
| Molding Shrinkage - Flow | 0.25 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness 1 | 104 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 126 | MPa | Internal method |
| Tensile Elongation (Break) | 1.8 | % | Internal method |
| Flexural Modulus | 8500 | MPa | Internal method |
| Flexural Strength | 174 | MPa | Internal method |
| Coefficient of Friction | 0.37 | Internal method | |
| Abrasion - Width | 6 | mm | Internal method |
| Abrasion Loss 2 | 4.5 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 11 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 266 | °C | Internal method |
| Melting Temperature | 281 | °C | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 2 to 8hr |
| Note Message | |
|---|---|
| 1 . | HR |
| 2 . | 120 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C24UST6L | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| Celanex® 1700FC | Celanese Corporation | PBT | Celanex® |
| COSMOPLENE® AX764 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| Forprene® 6NM901A45 | SO.F.TER. SPA | TPV | Forprene® |
| LNP™ THERMOCOMP™ RF00CSXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |