ExxonMobil™ PP8013L1
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wmgtiW_ExxonMobil-PP8013L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| An impact-resistant copolymer resin containing a nucleating agent having high impact strength at low temperatures. It is suitable for molding occasions such as containers and basins and other hard packaging, tools and boxes. It is also suitable for use as a composite modified substrate. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 920 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 17.2 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.2 | % | ISO 527-2/50 |
| Flexural Modulus | 890 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | ISO 179/1eA |
| 0°C | 14 | kJ/m² | ISO 179/1eA |
| 23°C | 56 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 54 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 73.3 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.9 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 137 | °C | ISO 306/A50 |
| Legal statement |
|---|
| 本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC7-7010RF | Spartech Polycom | PC | Spartech |
| APICAL 300AF929 | Kaneka Corporation | PI, TS | APICAL |
| Fortron® 1130L0 | Celanese Corporation | PPS | Fortron® |
| Keysor PVC KR247 | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| LNP™ THERMOCOMP™ DF0081PI compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |