Gramid N200GL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Grand Pacific Petrochemical Corporation |
| Trademark: | Gramid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wmPBmx_GramidN200GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Gramid N200GL is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in Europe or the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.4 | % | ISO 294-4 |
| Flow | 1.4 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 15512 |
| Relative Viscosity | 2.7 | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 86.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (2.00 mm) | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | -3.3 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD0490 | Qenos Pty Ltd | HDPE | Qenos PE |
| Adsyl 6 C 30 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| Electrafil® TPX-PC-02071 | Techmer Engineered Solutions | PC | Electrafil® |
| EPO-TEK® GE116 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Sylvin 8940-65 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |