SABIC® HDPE B4520
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wlV2cv_SABIC-HDPE-B4520-88273.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B4520 is typically used for blow moulding packaging up to 20 l, combining medium stiffness with a superior ESCR. This grade is suitable for packaging aggressive detergents and technical articles such as, spare fuel tanks, air- and cable ducts. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.16 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 20 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.89 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(75°C, 1.00 mm, Rhodacal-DS10) | 40.0 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C, Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 800 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 23°C, 2.00mm, molded | 22.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 23°C, 2.00mm, molded | 31.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 850 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 22.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/A | ||
| -30°C, molded | 5.0 | kJ/m² | ISO 180/A |
| 23°C, molded | 12 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 73.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 126 | °C | ISO 306/A |
| Melting Temperature (DSC) | 130 | °C | ISO 11357-3 |
| Enthalpy Change | 181 | J/g | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 3 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-7021U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Sinvicomp SRF3705Z | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TECAMID™ HS | Ensinger Inc. | Nylon 66 | TECAMID™ |
| INEOS HDPE T60-800-119 | INEOS Olefins & Polymers USA | HDPE | INEOS HDPE |
| Tunhe PET TH102B | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |