RX® 1-520
| Category: | DAP , Diallyl Phthalate |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | RX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wkQ8Xc_RX-1-520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RX® 1-520 is a short glass fiber reinforced, non-flame retardant, diallyl ortho-phthalate molding compound, which meets the requirements of ASTM D5948 Type SDG. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.83 | g/cm³ | ASTM D792 |
| Apparent Density | 0.75 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.10 to 0.30 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Compression Molded) | 76.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 12400 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 124 | MPa | ASTM D790 |
| Compressive Strength | 150 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 205 | °C | ASTM D648 |
| CLTE - Flow | 2.1E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.28 | W/m/K | ASTM C518 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 12 | kV/mm | ASTM D149 |
| Dielectric Constant 1 | ASTM D2520 | ||
| 1 kHz | 4.00 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor 2 | ASTM D150 | ||
| 1 kHz | 9.0E-3 | ||
| 1 MHz | 0.016 | ||
| Arc Resistance | 130 | sec | ASTM D495 |
| Comparative Tracking Index | > 600 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 26 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Wet |
| 2 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN ANC100 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Nanjing Hongrui PA66 A3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Cevian®-V VF191 | Daicel Polymer Ltd. | ABS | Cevian®-V |
| Dugdale PVC Rigid Extrusion Black Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| MAJ'ECO DFRG178G - 1199 | AD majoris | Biodeg Polymers | MAJ'ECO |