TOPAS® 8007F-600 Datasheet,COC,Topas Advanced Polymers, Inc.-SHANGHAI SUSHENG

TOPAS® 8007F-600

Category:	COC , Cyclic Olefin Copolymer
Manufacturer:	Topas Advanced Polymers, Inc.
Trademark:	TOPAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wi2NXQ_TOPAS-8007F-600.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Product Description TOPAS 8007F-600 is a new robust film extrusion grade designed for blending with polyethylene (PE). It is an improved clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Selected Applications Forming films (header bags, etc.) Protective packaging Shrink films and labels Twist films Decorative sheet Food packaging Food contact Leading Attributes Clarity, forming, barrier, purity, halogen-free Stiffness for downgauging, improved forming High shrink, low stress, gloss, toughness Outstanding deadfold, clean cutting Stiffness, chemical resistance, forming, even draw Not manufactured with BPA, phthalates, or halogens Broad regulatory compliance Related Grades for Packaging and Film Extrusion TOPAS 8007F-04 - ultimate clarity extrusion grade TOPAS 8007F-400 - robust extrusion grade especially for PE blends

Message

Product Description
TOPAS 8007F-600 is a new robust film extrusion grade designed for blending with polyethylene (PE). It is an improved clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in both cast and blown processes, and in monolayer and multilayer products. Leading film applications include twist wrap, forming webs, protective packaging, shrink films and labels, and easy tear packaging. Industrial uses include formed PE and PP sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.

Selected Applications

Forming films (header bags, etc.)

Protective packaging

Shrink films and labels

Twist films

Decorative sheet

Food packaging

Food contact

Leading Attributes

Clarity, forming, barrier, purity, halogen-free

Stiffness for downgauging, improved forming

High shrink, low stress, gloss, toughness

Outstanding deadfold, clean cutting

Stiffness, chemical resistance, forming, even draw

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

TOPAS 8007F-04 - ultimate clarity extrusion grade

TOPAS 8007F-400 - robust extrusion grade especially for PE blends

General Information
Features	High purity Moisture proof Rigidity, high Highlight Copolymer Good chemical resistance Good toughness Compliance of Food Exposure High shrinkage General BPA-free amorphous Halogen-free Medium transparency
Uses	Packaging Films Label Multilayer film Mixing cast film Sheet Food packaging General
Agency Ratings	DMF 12132 FDA FCN 405 Europe 10/1/2011 12:00:00 AM
Forms	Particle
Processing Method	Film extrusion Blow film cast film Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.01	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	1.8	g/10 min	ISO 1133
230°C/2.16 kg	10	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR)			ISO 1133
190°C/2.16 kg	2.00	cm³/10min	ISO 1133
230°C/2.16 kg	11.0	cm³/10min	ISO 1133
Water Absorption (Saturation, 23°C)	0.010	%	ISO 62

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	70	µm
Tensile Modulus			ISO 527-3/1
MD : 70 µm, cast film	2100	MPa	ISO 527-3/1
TD : 70 µm, cast film	1700	MPa	ISO 527-3/1
Tensile Stress			ISO 527-3/50
MD : Fracture, 70 µm, cast film	55.0	MPa	ISO 527-3/50
TD : Fracture, 70 µm, cast film	50.0	MPa	ISO 527-3/50
Tensile Elongation			ISO 527-3/50
MD : Fracture, 70 µm, cast film	3.4	%	ISO 527-3/50
TD : Fracture, 70 µm, cast film	3.4	%	ISO 527-3/50
Water Vapor Transmission Rate (70 µm, 23°C, Cast Film, 85% RH)	0.10	g·mm/m²/atm/24 hr	ASTM F1249

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	78.0	°C	ISO 11357-2

Optical	Nominal Value	Unit	Test Method
Gloss (60, 70.0 µm, cast film)	> 100		ISO 2813
Haze (70.0 µm, cast film)	> 2.0	%	ISO 14782

Extrusion	Nominal Value	Unit
Feed part of extruder	20 - 60	°C
Extruder Screw L/D Ratio	> 28:1
Cylinder Zone 1 Temp.	200 - 210	°C
Cylinder Zone 2 Temp.	200 - 210	°C
Cylinder Zone 3 Temp.	200 - 210	°C
Cylinder Zone 4 Temp.	200 - 210	°C
Die Temperature	220 - 230	°C

Extrusion instructions
Head pressure: P > 140 bar / 2000 psi; Fine screen packs as neededScrew speed: RPM > 50% nominalScrew design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 inch Grooved Feed: Hot temperature: 120°C (248°F)

Resin Grade	Manufacturer	Category	Trademark
WEVO-CHEMIE Polyurethanes PU 925/71 FL/900	WEVO-CHEMIE GmbH	PUR, Unspecified	WEVO-CHEMIE Polyurethanes
Multilon® TN-3713B	TEIJIN LIMITED	PC+ABS	Multilon®
4LAC® 25H23100	4Plas	ABS	4LAC®
HOPELEN SJ-160	Lotte Chemical Corporation	PP Homopolymer	HOPELEN
Luxus PP 16052	Luxus Limited	PP, Unspecified	Luxus PP

Resin Grade

Manufacturer