Order Products : sales@su-jiao.com
Durethan® BM 240 H2.0 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | whPTNC_Durethan-BM-240-H2-0-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % mineral, injection molding, heat-aging stabilized, low tendency to warp, isotopic properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.46 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.46 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ||||
| Across Flow : 280°C, 3.00 mm 1 | 1.2 | -- | % | ISO 2577 |
| Across Flow : 120°C, 2 hr, 3.00 mm 2 | 0.20 | -- | % | ISO 294-4 |
| Flow : 280°C, 3.00 mm 3 | 1.3 | -- | % | ISO 2577 |
| Flow : 120°C, 2 hr, 3.00 mm 4 | 0.17 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 210 | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 6000 | 2000 | MPa | ASTM D638 |
| 23°C | 6000 | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Break, 23°C | 84.8 | 50.3 | MPa | ASTM D638 |
| Break, 23°C | 85.0 | 50.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Break, 23°C | 9.0 | 35 | % | ASTM D638 |
| Break, 23°C | 7.0 | 40 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 5400 | 1800 | MPa | ASTM D790 |
| 23°C 6 | 5500 | 2100 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 155 | 64.8 | MPa | ASTM D790 |
| 3.5% Strain 7 | 140 | 50.0 | MPa | ISO 178/A |
| 23°C 8 | 150 | 60.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 9(23°C) | 5.0 | 8.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 10 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-060, MD40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 11 | 1.60 | -- | J | |
| -- 12 | 9.20 | -- | J | |
| Film Puncture Force | ISO 6603-2 | |||
| -- 13 | 825 | -- | N | |
| -- 14 | 3050 | -- | N |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | |
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 90 | kJ/m² | |
| 23°C | 120 kJ/m² | No Break | ||
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | 37 | 37 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 64 | 80 | J/m | ASTM D256 |
| -40°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 75 | 85 | kJ/m² | |
| 23°C | 100 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed, 3.99 mm | 200 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.99 mm | 105 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 50.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ISO 306/B50 |
| -- | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 15 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 to 1.0E+15 | 1.0E+12 to 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 35 | 38 | kV/mm | |
| 23°C, 3.00 mm | 35 | 35 | kV/mm | |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 16 | 5.00 | 15.0 | ||
| 23°C, 1 MHz 17 | 4.00 | 4.00 | ||
| 23°C, 100 Hz | 4.40 | 15.0 | ||
| 23°C, 1 MHz | 4.00 | 4.70 | ||
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.011 | 0.25 | ||
| 23°C, 1 MHz | 0.015 0.015 | 0.10 0.070 | ||
| Comparative Tracking Index | ||||
| Solution A | 525 | -- | V | IEC 60112 |
| -- | -- | 575 | V | ASTM D3638 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 18 | 26 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 500 Bar |
| 2 . | 150x150x3 |
| 3 . | 150x150x3; MT 80°C; 500 Bar |
| 4 . | 150x150x3 |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Pull Rate: 2 mm/min; 50% RH |
| 10 . | US-FMVSS302 |
| 11 . | -30°C |
| 12 . | 23°C |
| 13 . | -30°C |
| 14 . | 23°C |
| 15 . | 10°C/min |
| 16 . | Tinfoil Electrodes |
| 17 . | Tinfoil Electrodes |
| 18 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoflex S454 | Ravago Group | ABS | Sicoflex |
| CoREZYN® COR75-AQ-010L | Interplastic Corporation | Vinyl Ester | CoREZYN® |
| DURANEX® 2000 | Polyplastics Co., Ltd. | PBT | DURANEX® |
| KumhoSunny PC/PET KCA9361 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PET | KumhoSunny PC/PET |
| LNP™ THERMOCOMP™ KF005 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |