Tenac™-C SG454
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wh2CAf_Tenac--C-SG454.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C SG454 is an Acetal (POM) Copolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C SG454 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.6 to 2.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 32.0 | MPa | ISO 527-2 |
| -- | 32.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 90 | % | ASTM D638 |
| Break | 80 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1250 | MPa | ASTM D790 |
| -- | 1300 | MPa | ISO 178 |
| Flexural Strength | 51.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 153 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 74.0 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 50 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Mylar® J (375 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Badamid® LA70 GF30 | Bada AG | Nylon 66 | Badamid® |
| HiFill® ABS GF15 | Techmer Engineered Solutions | ABS | HiFill® |
| OTECH TPO OTE6519 - Cord Insulation | OTECH Corporation | TPO | OTECH TPO |