FORMULA P COMP 6220 M1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wgGvKI_FORMULA-P-COMP-6220-M1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FORMULA P COMP 6220 M1 is a polypropylene product,. It is available in Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | ISO 527-2 |
| Fracture | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 25 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 240 | °C | |
| Mold Temperature | 30.0 - 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 7010 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| NEFTEKHIM PP 7445LM | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Adell Polyolefin ZR-37 | Adell Plastics, Inc. | Polyolefin, Unspecified | Adell Polyolefin |
| Lumid® HI5001AH | LG Chem Ltd. | Nylon+Olefin | Lumid® |
| PLUSTEK PA301G7 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |