| Radiopaque compound based on Polyamide 12 (PA 12). Metallic filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 4.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 0.90 | % | |
| Flow : 2.00 mm | 0.70 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.70 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3(23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 4(23°C) | 55 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 165 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 7.0E+3 | ohms·cm | ASTM D257 |
| Electromagnetic Reflection | 74 | % | ASTM EST-83 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Half Value Thickness | Internal Method | ||
| -- 5 | 660.0 | µm | |
| -- 6 | 340.0 | µm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 80x10x4 mm |
| 3 . | 80x10x4 mm |
| 4 . | 63.5x12.7x3.2 mm |
| 5 . | 120 kV |
| 6 . | 80 kV |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ PX9406P resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Chemical Resources LLD100929 | Chemical Resources, Inc. | LLDPE | Chemical Resources |
| Daelim Po1y® LD-26A | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| DynaMix™ 1804-BLK | Polymer Dynamix | Acetal (POM) Copolymer | DynaMix™ |
| LNP™ THERMOCOMP™ 2C004 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |