Dynaflex™ G7410-1000-00

Category: TPE , Thermoplastic Elastomer
Manufacturer: PolyOne Corporation
Trademark: Dynaflex™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: wff2Oe_Dynaflex-G7410-1000-00.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Dynaflex™G7410-1000-00 is a high-performance composite material that is easy to process and is designed for various applications that require materials to be tough and durable.
  • Excellent coloring
  • Excellent thermal stability
  • It can be bonded to polypropylene by overlapping molding
  • Suitable for outdoor use
General Information
Features
  • Recyclable materials
  • Good coloring
  • Thermal stability, good
Uses
  • overmolding
  • Outdoor application
RoHS Compliance
  • RoHS compliance
Appearance
  • Natural color
Forms
  • Particle
Processing Method
  • Extrusion
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 0.898g/cm³ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)2.0g/10 minASTM D1238
Molding Shrinkage - Flow 1.8 - 2.2%ASTM D955
HardnessNominal ValueUnitTest Method
Durometer Hardness (Shore A, 10 sec)68ASTM D2240
ElastomersNominal ValueUnitTest Method
Tensile Stress 1ASTM D412
    100% strain, 23°C 22.69MPaASTM D412
    300% strain, 23°C 33.55MPaASTM D412
Tensile Strength (Break, 23°C)5.17MPaASTM D412
Tensile Elongation (Break, 23°C)500%ASTM D412
Tear Strength 28.0kN/mASTM D624
Compression Set (23°C, 22 hr)19%ASTM D395B
Fill AnalysisNominal ValueUnitTest Method
Apparent Viscosity (200°C, 11200 sec^-1)14.8Pa·sASTM D3835
Additional Information
Dynaflex™ G7410-1000-00 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.
InjectionNominal ValueUnit
Suggested Max Regrind 20%
Rear Temperature 166 - 204°C
Middle Temperature 177 - 216°C
Front Temperature 182 - 221°C
Nozzle Temperature 182 - 221°C
Mold Temperature 15.6 - 26.7°C
Back Pressure 0.345 - 1.03MPa
Screw Speed 25 - 75rpm
Injection instructions
以聚丙烯 (PP)、乙烯醋酸乙烯共聚物 (EVA) 或低密度聚乙烯 (PE) 为基础的色母料最适合 Dynaflex™ G7410-1000-00 着色。使用熔体流动速率较高(范围为 25 - 40 克/10 分钟)的色母料,则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%(重量)。可以使用液体颜料,但以矿物油为基础的载体对最终硬度值会有显著的影响。不应采用以 PVC 为基础的色母料。若使用 GLS 可供的预着色复合材料,则可达到较好的配色一致性。色母料是否适用,应由用户通过试验来最终确定。在使用此产品之前或之后,均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Dynaflex™ G7410-1000-00 可利用高达 20% 的回收料同时其性能所受影响却极小,但该回收料必须是未受到污染的。回收料的有效性应由用户最终确定。Dynaflex™ G7410-1000-00 具有极好的熔体稳定性。如果机器闲置三十 (30) 分钟或以上,则应将机筒排空。不需要干燥注射速度:1 - 5 英寸/秒第一阶段 - 提升压力:250 - 650 psi第二阶段 - 保持压力:70% 的升压保持时间(厚部件):4 - 10 秒保持时间(薄部件):1 - 3 秒
Note Message
1 .2 hours
2 .Mouth die c
3 .C mould
Resin Grade Manufacturer Category Trademark
tefanyl® VE VEIP 250 Mitsubishi Chemical Performance Polymers, Inc. PVC, Flexible tefanyl® VE
STRANOX PA6/45%LFT Oxford Polymers Nylon 6 STRANOX
FORMULA P ELAN 6003 UV Putsch Kunststoffe GmbH PP, Unspecified FORMULA P
LEXAN™ CFR9131 resin SABIC Innovative Plastics PC LEXAN™
Karina WHITE PVC COMPOUND 807D10/121-D-AC-LF Karina Ind. e Com. de Plásticos Ltda PVC, Unspecified Karina