| Flame Retardnat Polypropylene for Injection Moulding applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.4 - 2.0 | % | ASTM D955 |
| -- | 1.4 - 2.0 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 22.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 680 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 950 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 25.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 68.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 675 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CB70KA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Hy-Vin® VT795 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Dryflex® VE 75A101 | ELASTO | TPV | Dryflex® |
| 3M™ Dyneon™ Fluoroelastomer FE 5830Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Sylvin 9950-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |