LNP™ LUBRICOMP™ SFL36 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wfDEAw_LNP-LUBRICOMP-SFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP SFL36 is a compound based on PA 12 resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound SFL-4036 Product reorder name: SFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5900 | MPa | ISO 178 |
| Flexural Stress | 147 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 175 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 160 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP TPO TPO-2561 P Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| Braskem PP HP 525M | Braskem | PP Homopolymer | Braskem PP |
| EverGlide® MB125 | Polymer Dynamix | PP, Unspecified | EverGlide® |
| Karina CLEAR PVC COMPOUND 70/201-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ULTEM™ HU1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |