AEI SX-0410:CM401
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | weqAIA_AEI-SX-0410-CM401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ambient cure, silane crosslinkable, polyethylene for low voltage power cable insulation This crosslinkable polyethylene compound is designed for the insulation of power cables and heating cables; possessing outstanding extrusion properties at high output rates. The graft component SX558 is mixed with the crosslinking catalyst masterbatch CM401 generally in the ratio 95:5. It can be cured at ambient temperatures and is specifically designed for small and sector shaped conductors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | BS 2782 620A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.4 | g/10 min | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 19.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 450 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (135°C, 168 hr) | 7.0 | % | IEC 60811-1-2 |
| Change in Tensile Strain at Break (135°C, 168 hr) | -7.0 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold bending (-70°C) | pass | IEC 60811-1-4 | |
| Thermoset 1 | IEC 60811-2-1 | ||
| Elongation under load, 20N/cm² : 200°C | % | IEC 60811-2-1 | |
| Permanent elongation after cooling | 0.0 | % | IEC 60811-2-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor- 50Hz (23°C) | 3.00E-4 | IEC 60250 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time - <100% Hot elongation 2 | |||
| 800.0 µm | 5.0 | day | |
| 1.50 mm | 14.0 | day |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (20°C) | > 1.0E+16 | ohms·cm | BS 6622 |
| Dielectric Strength (20°C) | 21 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 50 Hz) | 2.00 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Most modern thermoplastic extruders will process SX-0410:CM401 compounds, particularly if a screw suitable for polyethylene extrusion is available. |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| 2 . | Cure assessment (ambient cure at 20°C and 50% humidity) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BR13NT8521 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Vydyne® 64C-R | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ALTECH® PP-H A 4920/107 MR20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Bergamid™ A70 G15 TM-Z | PolyOne Corporation | Nylon 66 | Bergamid™ |
| OnForce™ LFT LF9200-5001 RS Natural | PolyOne Corporation | PPS | OnForce™ LFT |