Evoprene™ Super G 932
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | AlphaGary |
| Trademark: | Evoprene™ Super G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | weLpB6_Evoprene-Super-G-932.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Evoprene™ Super G compounds are high performance SEBS-based TPE materials. They are formulated with a special resin modifier which increases the size of the end blocks. They are also compounded in a special way to ensure maximum dispersion of the various ingredients. The larger end blocks increase the glass transition temperature (Tg) providing two major practical advantages over regular SEBS-based compounds: improved heat resistance and improved recovery properties. The improved heat resistance raises the service temperature over regular SEBS-based grades by 10-15 deg C (18-25 deg F) and improves injection moulding cycle times by allowing the parts to be demoulded at a higher temperature without distortion. The improved recovery properties, as measured by compression set, provide much better sealing characteristics as explained overleaf. These compounds do need higher processing temperatures for best results. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 2781 |
| Molding Shrinkage | 1.2 to 3.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 71 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 4.00 | MPa | ISO 37 |
| Tensile Stress (Yield) | 12.3 | MPa | ISO 37 |
| Tensile Elongation (Break) | 490 | % | ISO 37 |
| Tear Strength 1 | 35 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 22°C, 72 hr | 18 | % | |
| 70°C, 22 hr | 24 | % | |
| 100°C, 22 hr | 39 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| M-S Flow | 1.86 | MPa | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate | ||
| Vent Depth | 0.020 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 4060A | Colorite Polymers | PVC, Unspecified | Unichem |
| DENISTAT M 00U 09 E | Vamp Tech | Acetal (POM) Copolymer | DENISTAT |
| Plaslube® PA6 CF30 TS15 BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| Estane® TS92AP7 NAT 021 | Lubrizol Advanced Materials, Inc. | TPU-PC | Estane® |
| Sylvin 9067A-90 Grey 9166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |