| Properties shown below for this filled blend are typical for a 35% mica and glass fiber reinforced polypropylene homopolymer. This product satisfies many application needs. Special compounds are available. UV stabilization for improved weatherability available. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 56.0 | MPa | ASTM D638 |
| Flexural Modulus - Secant 2 | 4150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 153 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 140 | °C | ASTM D648 |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted.Filler Content, In-house #1003-02: 35% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 - 3.0 | hr | |
| Rear Temperature | 221 - 229 | °C | |
| Middle Temperature | 229 - 235 | °C | |
| Front Temperature | 229 - 241 | °C | |
| Nozzle Temperature | 221 - 243 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 10.3 | MPa | |
| Holding Pressure | 1.03 - 4.14 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 1.5 to 2.75 in/sZone 4 Temperature: 450 to 475°FHot Runner Temperature: 430 to 470°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GF 40 RM-M black (3534) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| ExxonMobil™ HDPE HYA 600 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| LightSpan® LS-3443 | NuSil Technology | Silicone | LightSpan® |
| RTP 399 X 141379 A | RTP Company | PC | RTP |
| LNP™ THERMOCOMP™ OF006A compound | SABIC Innovative Plastics | PPS | LNP™ THERMOCOMP™ |