ALCOM® AHT 530/40
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® AHT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wdUZEp_ALCOMAHT53040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM®AHT 530/40 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 12 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 111 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 80 - 90 | °C | |
| Hot air dryer | 80 - 90 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 3.0 - 6.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN72200 | LyondellBasell Industries | LDPE | Microthene® G |
| Taitacell EPS 321F | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| 4POM® 9I11230 H | 4Plas | Acetal (POM) Homopolymer | 4POM® |
| Jiangsu Sinarise PX900M | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Lumiloy® GN1306F | LG Chem Ltd. | PPE+PS | Lumiloy® |