Polymer-E B231
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Asia Polymer Corporation (APC) |
| Trademark: | Polymer-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wdQggZ_Polymer-E-B231.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polymer-E B231 is a Low Density Polyethylene product. It is available in Asia Pacific. Applications of Polymer-E B231 include film and packaging. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 2.5 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 49 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | < 0.12 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Blown Film | 98.1 | MPa | |
| 1% Secant, TD : 32 µm, Blown Film | 177 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 21.6 | MPa | |
| TD : Break, 32 µm, Blown Film | 19.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 380 | % | |
| TD : Break, 32 µm, Blown Film | 550 | % | |
| Dart Drop Impact (32 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 31.8 µm | 53.9 | kN/m | |
| TD : 31.8 µm | 68.6 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 48.0 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 106 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°, 31.8 µm, Blown Film) | 100 | ASTM D523 | |
| Haze (31.8 µm, Blown Film) | 6.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayblend® R-FR610 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Hyundai EP PA6 LS180 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Lucel® HI515W | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| LUVOCOM® 1105-8052/EM/BL VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| PEARLSTICK® 45-40/19 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |