Ketron® PEEK-HPV
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Ketron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wdLZxE_Ketron-PEEK-HPV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ketron® PEEK-HPV is a Polyetheretherketone (PEEK) product. It is available in Europe. Typical application: Engineering/Industrial Parts. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.050 | % | |
| Saturation, 23°C | 0.30 | % | |
| Equilibrium, 23°C, 50% RH | 0.14 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 3.00 mm 1 | 0.11 | % | |
| 23°C, 3.00 mm 2 | 9.0 | mg | |
| 23°C, 3.00 mm 3 | 4.0 | mg |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 85 | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 215 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/1B/5 |
| Compressive Stress | ISO 604/1 | ||
| 2% Strain | 67.0 | MPa | |
| 1% Strain | 34.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 4 | 250 | °C | |
| -- 5 | 310 | °C | |
| Melting Temperature (DSC) | 340 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 3.5E-5 | cm/cm/°C | |
| 23 to 150°C | 4.0E-5 | cm/cm/°C | |
| > 150°C | 8.5E-5 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.24 | W/m/K |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | 43 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | Weight, 96 hrs |
| 3 . | Weight, 24 hrs |
| 4 . | 20000 hrs |
| 5 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3140-22 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Sylvin 9743-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trithene® CX 7065 | Petroquimica Triunfo | LDPE | Trithene® |
| Unichem 8045 | Colorite Polymers | PVC, Unspecified | Unichem |
| K-Resin® SBC KR53 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |