DynaMix™ XP-66LGR
| Category: | Nylon 66 Alloy , Polyamide 66 Alloy |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaMix™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wctY0A_DynaMix-XP-66LGR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass Filled PA 66 Alloy Features:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 1 | 18600 | MPa | |
| -- | 23800 | MPa | |
| Tensile Strength | ASTM D638 | ||
| Break 2 | 193 | MPa | |
| Break | 293 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break 3 | 3.4 | % | |
| Break | 2.3 | % | |
| Flexural Modulus | ASTM D790 | ||
| -- 4 | 15500 | MPa | |
| -- | 20700 | MPa | |
| Flexural Strength 5 | 310 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -- 6 | 1500 | J/m | |
| -- | 130 | J/m | |
| Unnotched Izod Impact | ASTM D256 | ||
| -- 7 | 120 | J/m | |
| -- | 1200 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 250 | °C | ASTM D648 |
| Melting Temperature | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| 2 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| 3 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| 4 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| 5 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| 6 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| 7 . | 50% Rh specimen accelerated conditioning was conducted in accordance to modified ISO-1110 procedure Specimens were conditioned in sealed chamber at 70°C and 50% Rh for at least 2 weeks. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 Z | RTP Company | PBT | RTP |
| Vi-Chem PVC VNC80-30I | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Kepamid® 2300VT | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Hostacom TKC451N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| PETOPLEN EH 161 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |