Ateva® 2821A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wcmLdk_Ateva-2821A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for extrusion coating, coextrusion, and specialty lamination applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 28.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 850 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 70.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-5343 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Karina WHITE PVC COMPOUD -E 811-10/184-Y-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TOTAL Polyethylene Bio TPSeal® 0750_05 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |
| 3M™ Dyneon™ PTFE Compound FC 18050 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LNP™ LUBRICOMP™ HFG25Z compound | SABIC Innovative Plastics | Nylon 11 | LNP™ LUBRICOMP™ |