Badadur® PBT8 TM-Z3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wcOCDH_Badadur-PBT8-TM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, standard injection moulding grade with good mechanical properties |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.42 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 1720 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 5.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Stress 5(23°C) | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 6 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed 7 | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed 8 | 45.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 9 | 223 | °C | ISO 3146 |
| Linear thermal expansion coefficient 10 | ISO 11359-2 | ||
| Flow | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 12 | > 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity 13(1 MHz) | 3.30 | IEC 60250 | |
| Dissipation Factor | 0.020 | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Additional Information |
|---|
| Maximum Service Temperature, IEC 216, some hours: 135CMaximum Service Temperature, IEC 216, 20000: 100°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 80 x 10 x 4 mm |
| 6 . | 80 x 10 x 4 mm |
| 7 . | 110 x 10 x 4 mm |
| 8 . | 110 x 10 x 4 |
| 9 . | 10 K/min, Compound for moulding |
| 10 . | >=10x10x4 mm |
| 11 . | 80 x 80 x 1 mm |
| 12 . | 80 x 80 x 1 mm |
| 13 . | 80 x 80 x 1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 33MBTU | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SILVER® SA-5301 | Guangdong Silver Age Sci & Tech. Co., Ltd | Polyolefin, Unspecified | SILVER® |
| NEMCON H PC/ABS DP182 | Ovation Polymers Inc. | PC+ABS | NEMCON H |
| Karina IVORY PVC COMPOUND -E 90900-35/1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LITEN VL 10 | UNIPETROL RPA | PE Copolymer | LITEN |