Order Products : sales@su-jiao.com
RTP 2199 X 134911 A
| Category: | PEI , Polyether Imide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wcGZZB_RTP-2199-X-134911-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nickel-Coated Carbon Fiber - Stainless Steel Fiber - Electrically Conductive - EMI/RFI Shielding - (Preliminary Data Sheet) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.050 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ASTM D638 |
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 13800 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+4 | ohms | ASTM D257 |
| -- | < 1.0E+3 | ohms | ESD STM11.11 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 371 - 399 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARODUR 100 | Taro Plast S.p.A. | ABS | TARODUR |
| Niuk YPC5008 | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| HIDEN® A015E IS | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| LUVOCOM® 19-7745 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| MAXATEL® AC800AVL-NAT | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |