LNP™ LUBRICOMP™ KFI15 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wcA68f_LNP-LUBRICOMP-KFI15-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KFI15 is a compound based on Acetal containing 25% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KFL-4415 Product reorder name: KFI15 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.56 | g/cm³ | |
| -- | 1.50 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption (24 hr, 50% RH) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9260 | MPa | ASTM D638 |
| -- | 8720 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 112 | MPa | ASTM D638 |
| Break 3 | 102 | MPa | ASTM D638 |
| Break | 118 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Break 5 | 2.0 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 7850 | MPa | ASTM D790 |
| -- 7 | 8020 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 172 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 180 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 176 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 76 | J/m | ASTM D256 |
| 23°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 540 | J/m | ASTM D4812 |
| 23°C 11 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 163 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 163 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 159 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styropor® BFL 397 | BASF Corporation | PS (EPS) | Styropor® |
| ExxonMobil™ HDPE HD 6706 Series | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Karina GREEN COLOR CONCENTRATE 40/482-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifor® 5020/V2-EP NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| POLYFLAM® RPP 4225 CS1 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |