Spartech Polycom F5134T2-4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wbyAMg_Spartech-Polycom-F5134T2-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech Polycom F5134T2-4 is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 30 | % | ASTM D638 |
| Flexural Modulus - Secant | 1830 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 36 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 121 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.6 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProPell™ PEBA 72D 3083651 | Foster Corporation | Unspecified | ProPell™ |
| ACCUTECH™ HP0339C20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Daelim Po1y® LH-3250 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| LEXAN™ ML7696 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| MAJORIS HPS X790 | AD majoris | PPS | MAJORIS |