Zytel® 70G33L NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wZekNC_Zytel-70G33L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% Glass Reinforced Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.1 | -- | % | ISO 294-4 |
| Flow direction | 0.30 | -- | % | ISO 294-4 |
| Water Absorption | ||||
| 24 hr | 1.2 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 5.7 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.8 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 5.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 8000 | MPa | ISO 899-1 |
| 1000 hr | -- | 5500 | MPa | ISO 899-1 |
| Flexural Modulus | 9300 | 6210 | MPa | ISO 178 |
| Flexural Stress | 290 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 75 | kJ/m² | ISO 179/1eU |
| 23°C | 85 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 10 | 10 | kJ/m² | ISO 180/1A |
| -30°C | 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C | 12 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 70 | 70 | kJ/m² | ISO 180/1U |
| 23°C | 80 | 90 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 252 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.3E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat Capacity | 1330 | -- | J/kg/°C |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Specific Heat Capacity of Melt | 2210 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.22 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.20 | -- | IEC 60250 | |
| 1 MHz | 4.00 | -- | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.010 | -- | IEC 60250 | |
| 1 MHz | 0.015 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | 28 | -- | mm/min | ISO 3795 |
| Flammability Classification (0.710 mm) | HB | -- | IEC 60695-11-10, -20 | |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | SE/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex NT0620GB | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| UBESTA 3030 JLX2 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Durethan® AKV 35 H3.0 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |
| ELASTOSIL® R plus 4000/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| NORYL™ SE1X resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |