Rotuba CAB B908 (13% Plasticizer)
| Category: | CAB , Cellulose Acetate Butyrate |
| Manufacturer: | Rotuba Extruders, Inc. |
| Trademark: | Rotuba CAB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wZCOk2_RotubaCABB90813Plasticizer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rotuba CAB B908 (13% Plasticizer) is a cellulose acetate butyrate (CAB) product,. It can be processed by injection molding and is available in North America. Rotuba CAB B908 (Plasticizer 13%) has applications including optics/lenses, automotive industry, commercial/office supplies, consumer goods and handles. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.4 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 24.8 | MPa | ASTM D638 |
| Fracture | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Flexural Strength | 32.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 68.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 221 | °C | |
| Mold Temperature | 52 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® M368 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| SEETEC PP R3450 | LG Chem Ltd. | PP Random Copolymer | SEETEC PP |
| Wellamid® MRGF25/15 42H-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| KOPLA PC KTE1707 | KOPLA Co., Ltd. | PC+PBT | KOPLA PC |
| LNP™ THERMOCOMP™ RF003H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |