Ecovio® M2351
| Category: | Copolyester , Copolyester |
| Manufacturer: | BASF Corporation |
| Trademark: | Ecovio® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wYtrnu_Ecovio-M2351.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ecovio® M2351 is our new biodegradable compound for film extrusion based on our biodegradable copolyester ecoflex® F Blend and polylactic acid (PLA). Due to its outstanding mechanical strength ecovio® M2351 offers a great down gauging potential needed for thin agricultural or horticultural film applications like mulch film, cover film, silage film and others. ecovio® M2351 already contains antiblocking agents required for easy processing on film extrusion and film conversion equipment. ecoflex® F Blend is the continuous phase in the structure of ecovio® M2351 transferring the beneficial film properties of ecoflex® F Blend into the new product. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 to 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 5.00 to 11.0 | cm³/10min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 12 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 12 µm, Blown Film | 260 | MPa | |
| TD : 12 µm, Blown Film | 130 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 12 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 12 µm, Blown Film | 18.0 | MPa | |
| MD : 12 µm, Blown Film | 25.0 | MPa | |
| TD : 12 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 12 µm, Blown Film | 180 | % | |
| TD : Break, 12 µm, Blown Film | 380 | % | |
| Dart Drop Impact (12 µm, Blown Film) | 200 | g | ASTM D1709A |
| Water Vapor Transmission Rate (38°C, 90% RH, 12 µm, Blown Film) | 1500 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | DSC | ||
| -- 1 | 110 to 120 | °C | |
| -- 2 | 140 to 155 | °C |
| Note Message | |
|---|---|
| 1 . | ecoflex® |
| 2 . | PLA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers Nylon 6604 HS | Network Polymers, Inc. | Nylon 66 | Network Polymers Nylon |
| FMC® 201 | Smooth-On, Inc | Polysulfide Rubber | FMC® |
| Grivory® HT1V-5 HY black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| HiFill® MD 90-80039 GY | Techmer Engineered Solutions | HDPE, HMW | HiFill® |
| POCAN® KU 2-7503/1 000000 | LANXESS GmbH | PBT | POCAN® |