ATTANE™ 4201G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wYbU3D_ATTANE-4201G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.912 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance (25 µm) | 31.4 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 25 µm | 138 | MPa | ASTM D882 |
| 2% secant, TD : 25 µm | 141 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 10.1 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 9.03 | MPa | ASTM D882 |
| MD : Break, 25 µm | 38.5 | MPa | ASTM D882 |
| TD : Break, 25 µm | 34.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 520 | % | ASTM D882 |
| TD : Break, 25 µm | 710 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 870 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 370 | g | ASTM D1922 |
| TD : 25 µm | 590 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.8 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 33 | ASTM D2457 | |
| Haze 1(25.4 µm) | 1.7 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：DBS II 模具间隙：70 密尔 (1.8 mm) 熔体温度：440-450°F (226-232°C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：75 rpm 冷冻线高度：25 英寸 |
| Note Message | |
|---|---|
| 1 . | Internal |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Armor-X™ Non-Marring | Quadrant Engineering Plastic Products | TP, Unspecified | Quadrant EPP |
| Tenopom® POM B3 M3 NTLA014 PR301 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| UMG WOOD® W900A | UMG ABS, Ltd. | ABS | UMG WOOD® |
| ELASTOSIL® RT 708 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Durethan® BKV 140 H2.0 DUS008 900051 | LANXESS GmbH | Nylon 6 | Durethan® |