Tecodur® PB70 GR20 NL100 HS
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecodur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wXSqUn_Tecodur-PB70-GR20-NL100-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 20% glass fiber reinforced, heat stabilized, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.1 | % | |
| Flow | 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 0.080 | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Hopper Temperature | 50.0 to 70.0 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 to 80.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 70A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| Stat-Tech™ ST7300-8045 EI OOV GREY6 | PolyOne Corporation | ABS | Stat-Tech™ |
| Baydur® 726 IBS (40 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Armlen® PP TM 40-1 | Poly Plastic | PP, Unspecified | Armlen® |
| Hipolyene 8501 T6 B | Zylog Plastalloys | TPO (POE) | Hipolyene |