ACCUTECH鈩?HP0339M10CL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wWf79h_ACCUTECH-HP0339M10CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0339M10CL is a polypropylene homopolymer (PP Homopoly) product, which contains 10% mica filler. It is available in North America. The main characteristics are: chemical coupling. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.0958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 37.0 | MPa | ASTM D638 |
| Fracture | 32.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 17 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 63.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3960 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SynPlast™ 901P-N | PolyOne Corporation | Di (Nonyl, Decyl, Undecyl) Phthalate | SynPlast™ |
| UBE Polyethylene F019 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| LNP鈩?THERMOCOMP鈩?OF008G compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |
| Plexiglas® Resist zk6HC | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |